NLMK Verona Tool Steel DB6 (DIN 1.2714): Properties, Applications & Supply in India

If you own a forging shop, die-making unit or heavy tooling operation, you know that the difference between a die that lasts one production run and one that lasts hundreds comes down to the steel underneath it. NLMK Verona Tool Steel DB6 is one of the European grades that is increasingly being specified by Indian manufacturers for close die forging, hammer dies and heavy-impact tooling – and with good reason.

This guide will explain what NLMK Verona DB6 really is, its real composition and mechanical properties, how it machines and heat-treats, where it is used and how to decide if it is the right grade for your application – all from verified technical data.

What Is NLMK Verona Tool Steel DB6?

NLMK Verona Tool Steel DB6 is a specialty tool steel plant of the NLMK Group, located in the north of Italy, close to Verona. The plant produces forged blocks, plates, and ingots for tool and die applications, and currently supplies its hot-work die steel to the Indian market under the DB6 designation — the specific grade Virat Steels stocks and distributes from this mill.

DB6 is not a proprietary or obscure code. It corresponds to well-established international standards:

Designation	Standard
DB6	Commercial/trade name
DIN 1.2714	German (Werkstoff) standard
AISI L6	American standard
AFNOR 55NCDVV7	French standard
Standard family	55NiCrMoV (Cr-Ni-Mo-V alloyed hot-work steel)

To summarize, a buyer searching for “NLMK Verona DB6”, “db6 nmlk verona” or “nmlk verona die steel” is looking for this specific chromium-nickel-molybdenum-vanadium alloyed hot-work die steel, a popular grade in the European and Indian tooling supply chains, now available from NLMK Verona’s Italian production.

Chemical Composition of NLMK Verona Tool Steel DB6 / DIN 1.2714

DB6 is a Cr-Ni-Mo-V alloy system which provides a balance of toughness and hardness:

Element	C	Si	Mn	P	S	Cr	Ni	Mo	V
% Range	0.50–0.60	0.10–0.40	0.65–0.95	≤0.03	≤0.03	1.00–1.20	1.50–1.80	0.45–0.55	0.07–0.12

DB6 has high toughness and impact resistance (compared to more common hot-work grades such as H13) and high nickel content (compared to more common hot-work grades such as H13) for exceptional toughness and impact resistance rather than pure high-temperature hardness retention.

Mechanical Properties

Property	Value
Tensile Strength	1000–1400 MPa
Yield Strength	1045 MPa
Elongation	15%–20%
Impact Toughness	20–25 J/cm²
Hardness (working)	50–55 HRC
Compressive Strength	2500 MPa
Modulus of Elasticity	205 GPa

Typical supply hardness ranges (depending on treatment condition):

Annealed condition: 255 BHN max
Hardened & tempered: 38–42 HRC (die-ready condition), with tools further hardened up to 50–55 HRC for service
Hardness variation, surface to core: 20–25 BHN

Physical Properties

Coefficient of Thermal Expansion (10⁻⁶ m/m·K)	20–100°C	20–200°C	20–300°C	20–400°C	20–500°C	20–600°C
Value	12.1	13.1	13.2	13.5	14.1	14.3

Thermal Conductivity (W/m·K)	20°C	350°C	700°C
Value	35.0	39.0	36.0

Note: Exact physical values can vary slightly with heat treatment and section size — always cross-check against the mill test certificate for critical applications.

Machinability of NLMK Verona DB6

DB6 is easy to work and the machinability can be rated at about 90 % relative to W-group water-hardening low-alloy steels taken as the 100 % reference. This makes it much easier to machine than many high-alloy cold-work or high-speed steel grades, and still retains the toughness needed for heavy forging dies.

Practical machining notes:

Best machined in the annealed condition (≤255 BHN) before final hardening
Finish machining should ideally be completed before final hardening and tempering, with only grinding/polishing done after
Stress-relief before hardening reduces distortion risk in large die blocks

Heat Treatment Guide

Process	Parameters
Annealing	Soak at 740–760°C, furnace-cool at max 10°C/hr down to 600°C, then air cool
Hardening	Preheat to 650°C, raise quickly to 900–950°C, quench in oil
Hardening (mill data)	840–880°C oil quench → 57 HRC; 860–900°C air quench → 55 HRC
Tempering	Multiple tempers; hardness drops from ~56 HRC (100°C temper) to ~34 HRC (650°C temper)
Stress Relieving	Heat to 600–650°C, soak 2 hrs per 25mm section, slow cool
Forging	Warm to 700°C, raise to 1050°C, keep forging above 800°C, cool slowly in furnace/vermiculite
Nitriding	Possible after hardening + tempering; done ~50°C above nitriding temperature
Normalizing	Not recommended — DB6 is air-hardening

Applications of NLMK Verona DB6 Tool Steel

DB6’s high toughness and impact resistance make it especially suited to heavy-impact forging applications rather than pure high-temperature die casting:

Dies for drop forging hammers & mechanical presses
Die holders, cassettes, and shoe blocks
Hot shear blades
Piston rods, cranks, and boosters
Punches and blanking/forming dies
Trimmer dies
Clutch parts, pawls, shafts, knuckle pins
Forming rolls, spindles, and rollers

Industries: Automotive component manufacturing, heavy forging, aerospace tooling, general engineering, and metalworking.

Advantages of NLMK Verona DB6 Tool Steel

Superior toughness and impact resistance compared to many hot-work alternatives — ideal where shock loading, not just heat, is the main stress
Good hardenability through thick sections, suited to large forging die blocks
European mill origin (NLMK Verona, Italy) with documented alloy composition
Good machinability (~90% relative rating) compared to many alloy tool steels
Nitriding-compatible for surface wear resistance without sacrificing core toughness
Supplied by Virat Steels with extra forging reduction, upsetting, and double tempering for improved ultrasonic quality in die blocks

DB6 vs H13 vs D2 — Comparison Table

Factor	DB6 (DIN 1.2714)	H13 (DIN 1.2344)	D2 (Cold Work)
Category	Hot-work, high-toughness	Hot-work, high-temp hardness	Cold-work, high wear resistance
Key strength	Toughness & impact resistance	Thermal fatigue resistance	Abrasion/wear resistance
Typical hardness	50–55 HRC	~50 HRC	58–62 HRC
Best suited to	Hammer/press forging dies, shock loading	Die casting, extrusion dies	Blanking, punching, cold forming
Machinability	Good (~90% rating)	Good	Moderate (high alloy content)
Nickel content	High (1.5–1.8%)	None	None

How to Choose Between NLMK Verona Tool Steel DB6 (and Other Grades)?

Is your tooling exposed to repeated impact/shock loading? DB6 is specifically strong here — hammer forging and heavy press dies benefit most from its toughness.
Is your process purely high-temperature (die casting, hot extrusion) with less shock? H13 (DIN 1.2344) may be a better fit than DB6 due to superior thermal fatigue resistance.
What supply condition do you need? DB6 is available annealed or hardened & tempered — confirm this at order stage based on your in-house heat treatment capability.
What section size does your die need? Large forged blocks require good through-thickness hardenability — DB6’s alloy design supports this.
Do you need surface hardening? DB6 can be nitrided after hardening/tempering for improved wear resistance while keeping core toughness.
Do you need ultrasonic-tested quality die blocks? Ask specifically for extra forging reduction and double-tempered blocks — Virat Steels supplies DB6 this way for critical forging applications.

Why Source NLMK Verona DB6 Through Virat Steels?

NLMK Verona origin DB6/DIN 1.2714 Steel – Official stockist and supplier
PAN-India supply network covering major forging & auto hubs (Ahmedabad, Pune, Chennai, Bengaluru, Delhi NCR, Ludhiana etc.)
Flat, square, and round bar available in project-based quantities
Extra forging reduction and double tempering for improved ultrasonic quality on die blocks
Technical support to confirm the right grade — DB6 vs H13 vs other die steels — for your specific application

Frequently Asked Questions

1. What is NLMK Verona Tool Steel DB6?
It is a Cr-Ni-Mo-V alloyed hot-work die steel (DIN 1.2714 / AISI L6) produced by NLMK Verona, Italy and supplied in India by Virat Steels.

2. What is DB6 steel equivalent to?
DB6 is commonly equivalent to DIN 1.2714, AISI L6, and AFNOR 55NCDVV7.

3. What is the hardness of DB6 steel?
Working hardness is typically 50–55 HRC after hardening and tempering; annealed condition is supplied at 255 BHN max.

4. Is DB6 better than H13 steel?
DB6 provides higher toughness and impact resistance, hence better suited for heavy forging, whereas H13 is more suitable for high temperature hot-work processes such as die casting.

5. Which steel is better for hammer forging dies?
DB6 is generally preferred for hammer forging dies due to its superior toughness and shock resistance.

6. What is the chemical composition of DB6?
Approximately 0.50–0.60% C, 1.00–1.20% Cr, 1.50–1.80% Ni, 0.45–0.55% Mo, and 0.07–0.12% V.

7. Can DB6 steel be welded or re-hardened?
Yes, but it must be done carefully — with stress tempering for pre-hardened condition — to avoid cracking.

8. Is DB6 steel suitable for hot work applications?
Yes, DB6 performs well in hot-work applications due to its strength and toughness at elevated stress conditions.

9. What is the machinability of DB6 steel?
DB6 rates roughly 90% machinability relative to W-group water-hardening steels (100% baseline) — considered good.

10. Should DB6 be normalized?
No — DB6 is air-hardening and should not be normalized.

11. Can DB6 be nitrided?
Yes, after hardening and tempering, at approximately 50°C above the intended nitriding temperature.

12. What shapes is NLMK Verona DB6 available in?
Flat, square, and round bar, supplied by Virat Steels across India.

13. Does Virat Steels supply NLMK Verona DB6 in India?
Yes, Virat Steels is a stockist and supplier of NLMK Verona-origin DB6/DIN 1.2714 tool steel.

14. What industries use DB6 tool steel?
Automotive components, heavy forging, aerospace tooling and general engineering.

15. What is the forging temperature range for DB6?

Heat to 700°C and then raise rapidly to 1050°C. Keep forging temperature above 800°C.

16. What’s the distinction between DB6 and DIN 2713?

The DIN 2713 is improved for better die performance and is called DIN 2714 (DB6).

17. What tensile and yield strength does DB6 offer?
Tensile strength 1000–1400 MPa, yield strength ~1045 MPa.

18. Does DB6 require oil or air quenching?
Both are used. Oil quenching at 840-880 °C gives ~57 HRC. Air quenching at 860-900 °C gives ~55 HRC.

19. What documentation should I request when ordering NLMK Verona DB6?
Always request a mill test certificate (MTC) confirming the heat/batch chemical composition and mechanical test results.

20. Where can I buy NLMK Verona DB6 tool steel in India?
Virat Steels supplies and stocks NLMK Verona DB6/DIN 1.2714 steel PAN-India, including to Gurugram, Delhi NCR, Pune, Chennai, and other major industrial hubs.

Conclusion

NLMK Verona Tool Steel DB6 (DIN 1.2714 / AISI L6) is the best solution for one simple reason: toughness where it counts – in heavy forging dies subject to repeated shock loading. Its Cr-Ni-Mo-V alloy design, excellent machinability and good hardenability make it a preferred choice for forging shops and die makers across India.

Need NLMK Verona DB6 die blocks, flats, squares, or round bars for your next forging project? Get in touch with Virat Steels — share your drawing and section size requirement, and our team will confirm grade, stock availability, and delivery timelines.

+91-98140 21775 | info@viratsteels.com

Hot Work Tool Steel: Grades, Properties, Hardness, Heat Treatment & Applications

Hot work tool steel is designed for one purpose – to resist heat that would ruin common steel. It is the material behind the dies, molds, punches and blades that are hammered and squeezed and repeatedly heated and cooled – in die casting, forging, extrusion, hot stamping and hot shearing.

And what makes it different is easy to say and hard to engineer. It keeps its hardness, toughness, strength and dimensional stability, even when it’s hot. The most common grades you’ll come across are H13 (DIN 1.2344), H11 (DIN 1.2343) and DB6 (DIN 1.2714) — which one you need depends on your operating temperature, impact load, die size and how long you want the tool to last.

What Is Hot Work Tool Steel?

It’s an alloy tool steel for tools that get hot and cycle between hot and cold, again and again. It must be a combination of hot hardness, toughness, wear resistance, thermal-fatigue resistance and dimensional stability — all at the same time.

The Three Grades You Should Know:

H13 / DIN 1.2344 – the go-to grade for die casting, aluminum extrusion and hot forging.
H11 / DIN 1.2343 — good balance of toughness and hot strength, for forging and extrusion.
DB6 / DIN 1.2714 – the choice for large forging dies, hammer dies and heavy-impact work where toughness is the most important property.

The final choice should always be based on the application and the steel maker’s datasheet, not on a general guide like this.

Hot work tool steel is a high-alloy steel for tooling operating at temperatures above about 200°C. Hot work grades are designed to resist the direct action of molten metal and hot workpieces, as opposed to cold-work steels, which are designed for cutting and forming at room temperature.

You will find it in aluminum and brass die-casting dies, forging dies, extrusion dies, hot shear blades, punches, mandrels, hot trimming dies, glass molds and copper alloy dies. It is their resistance to heat checking, deformation and softening that keeps these tools dimensionally stable and working reliably, cycle after cycle.

Popular Hot Work Tool Steel Grades

Steel Grade	DIN Standard	Equivalent	Common Applications
H13	1.2344	AISI H13 / JIS SKD61	Die casting, forging, aluminium extrusion
H11	1.2343	AISI H11 / JIS SKD6	Forging dies, aluminium dies, extrusion
DB6	1.2714	No exact AISI match; closest reference ~L6	Hammer dies, press dies, forging dies
H21	1.2581	AISI H21	High-temperature tooling
H10	1.2365	AISI H10	Hot-work applications
H12	1.2606	AISI H12	Hot-work applications

Mechanical Properties

Property	H13	DB6
Density	7.75–7.85 g/cm³	7.70–7.85 g/cm³
Tensile Strength	1550–2100 MPa	High
Hardness	44–54 HRC	38–42 HRC (working); refer to supplier datasheet
Toughness	Excellent	Excellent
Wear Resistance	Excellent	Excellent
Thermal Fatigue Resistance	Excellent	Excellent

Chemical Composition

The alloying elements are what actually give hot work tool steel its personality — hardness, toughness, wear resistance and how it behaves under heat.

Element	H13 (%)	DB6 (%)
Carbon (C)	0.32–0.45	0.50–0.60
Silicon (Si)	0.80–1.25	0.10–0.40
Manganese (Mn)	0.20–0.60	0.65–0.95
Chromium (Cr)	4.75–5.50	1.00–1.20
Molybdenum (Mo)	1.10–1.75	0.45–0.55
Vanadium (V)	0.80–1.20	0.07–0.12
Nickel (Ni)	—	1.50–1.80

Hardness (HRC Scale)

Hardness is usually the first thing buyers ask about and it is really a trade-off push hardness up and you get wear resistance but you risk giving up toughness and a tool that is too hard cracks before it wears out.

Grade	Typical Working Hardness
H13	44–54 HRC
H11	42–50 HRC
DB6 (1.2714)	38–42 HRC

DB6 is designed for lower working hardness than H13 tool steels – it is selected for hammer and large forging dies because it sacrifices some wear resistance for superior toughness, so it is tempered back further to prevent cracking under heavy impact.

Tip: The right hardness is not the hardest, it is the one that works for your application and duty cycle. Always verify the exact range with the datasheet of your supplier, as this may differ with section size and delivery condition.

How Hot Work Tool Steel Is Made

Good performance from hot work tool steel is not just a matter of choosing the right grade on paper – it is a matter of how well the steel was melted, forged, heat treated and inspected along the way.

1. Raw Material Selection

Everything starts with the alloying mix, and each element earns its place:

Element	Main Function
Carbon	Hardness and strength
Chromium	Wear resistance and hardenability
Molybdenum	High-temperature strength
Vanadium	Grain refinement and wear resistance
Nickel	Toughness
Silicon	Strength and heat resistance
Manganese	Strength and hardenability

2. Smelting & Refining

The steel is melted in an Electric Arc Furnace (EAF) and then further refined to the desired chemistry and cleanliness.

Ladle refining improves alloy composition, controls temperature and reduces contamination

Vacuum degassing removes dissolved gasses, mainly hydrogen, leading to better toughness, improved fatigue life, fewer internal defects and a more reliable material overall.

3. Electro-Slag Remelting (ESR)

ESR is a must when cleanliness and consistency counts. It provides a more homogeneous microstructure, better toughness and fatigue life, less segregation and a significantly improved polishability – which is why ESR grades are found in precision dies, high pressure die casting and plastic molds.

4. VAR (Vacuum Arc Remelting)

For the most demanding applications VAR takes purity one step further – lower inclusion levels, more uniform microstructure and better fatigue resistance.

5. Ingots casting

Molten steel is poured into ingots before forging, under controlled solidification conditions to minimize segregation and shrinkage.

6. Forging

Forging turns the cast ingot into dense blocks and bars by controlled heating and deformation. It increases the toughness, the grain structure, the internal flaws and gives more consistent mechanical properties to the material. Typical outputs are forged blocks, die blocks, round bars, flat bars and ESR blocks.

7. Annealing

Annealing is the process that softens the steel for machining and preparation for hardening — heat, soak evenly, then cool in a controlled fashion.

Grade	Approx. Annealed Hardness
H13	190–230 HB
H11	180–230 HB
DB6 (1.2714)	255 HB max

Hardening is the method by which steel is given strength and wear resistance. It involves controlled pre-heating, austenitising, soaking and controlled cooling or quenching.

Grade	Typical Austenitizing Range
H13	1,020–1,050°C
H11	1,000–1,030°C
DB6 (1.2714)	~850–900°C (typical for this Ni-Cr-Mo grade; noticeably lower than the Cr-Mo-V H-series)

DB6 is a lower alloy nickel chromium molybdenum steel and hardens at a substantially lower temperature than H13 or H11. Always stick to the manufacturer’s datasheet for the exact cycle – especially if you are working with large sections where getting this wrong is expensive.

9. Tempering

Tempering is done after hardening to reduce brittleness and to obtain the final balance between hardness and toughness. It relieves residual stress, increases toughness and helps dimensional stability. Depending on the grade, multiple cycles of tempering may be utilized.

Heat Treatment at a Glance

Stage	Purpose
Annealing	Improve machinability
Stress Relieving	Reduce machining stresses
Hardening	Increase hardness and strength
Tempering	Improve toughness and stability
Final Inspection	Verify required properties

10. Quality Inspection

The material is examined from every point of view before being shipped:

Ultrasonic Testing (UT) — identifies internal cracks, inclusions, laminations and shrinkage-related defects, especially important on large forged blocks.

Chemical composition testing – a spectrometer tests carbon, chromium, molybdenum, vanadium, nickel, silicon, manganese, sulfur and phosphorus against the specified grade.

Hardness and dimensional inspection: Rockwell or Brinell testing, checks of length, width, thickness, flatness, squareness, straightness and surface finish.

11. MTC (Material Test Certificate)

An MTC links grade, heat number, chemical composition, mechanical properties, hardness, heat-treatment condition, inspection results and manufacturer details. It provides buyers with a paper trail they can verify.

Document / Test	Purpose
MTC / EN 10204 3.1	Material traceability and test results
UT Report	Internal quality verification
Spectrometer Report	Chemical composition
Hardness Report	Hardness verification
Heat Number	Batch traceability
Dimensional Report	Size verification

Where Hot Work Tool Steel Is Used

Aluminum diecast molds H13 tool steel is the material of choice here because it can be repeatedly heated and cooled without losing dimensional stability – think engine blocks, gear housings, transmission components, pump bodies, LED housings and other automotive parts.

Hot-forging dies They are pounded by impact loads and heat, which is why DB6 and H11—valued for toughness and resistance to thermal cracking—are the usual choices. Common on crankshafts, connecting rods, railroad components and heavy engineering components.

Extrusion Dies High hot strength and wear resistance is needed to keep profiles – used for aluminum profiles, window frames, heat sinks and electrical conductors.

Brass and copper die cast. These alloys run hotter than aluminum so H13 and H11 earn their keep with better hot hardness.

Hot shear blades, for cutting red-hot blooms, billets and bars in rolling mills;

Hot punches, made for hot piercing, making and punching where wear and impact resistance both count.

Glass molds on the basis of thermal stability and resistance to heat checking.

Plastic mold parts: ESR H13 material tool preferred for polishability and wear resistance.

Industries That Rely on It

Industry	Applications
Automotive	Die casting, forging
Aerospace	Forging tools
Defence	Heavy-duty dies
Railways	Forged components
Aluminium	Extrusion dies
Plastic Moulding	Mould inserts
Steel Plants	Hot shear blades
Heavy Engineering	Forging tools
Energy	Turbine & valve tooling

Hot Work vs. Cold Work vs. Plastic Mould Steel

Feature	Hot Work Tool Steel	Cold Work Tool Steel	Plastic Mould Steel
Primary Use	High-temperature tooling	Room-temperature cutting/forming	Plastic injection & moulding
Operating Temperature	High	Low to moderate	Low to moderate
Key Property	Hot hardness & thermal fatigue resistance	Wear resistance & hardness	Toughness, polishability & machinability
Important Grades	H13, H11, DB6	D2, D3, EN31	P20, P20+Ni, 1.2083
Common Applications	Die casting, forging, extrusion	Dies, punches, blanking, shear blades	Injection moulds, plastic moulds
Typical Hardness	44–54 HRC	55–62 HRC	28–52 HRC
Main Advantage	Retains strength at elevated temperatures	Excellent wear & edge retention	Good machinability and surface finish
Typical Industries	Automotive, forging, die casting	Tool & die, automotive, engineering	Plastic, packaging, automotive

Parameter	H13	DB6
Type	Chromium hot work steel	Nickel-chromium-molybdenum tool steel
Hardness	44–54 HRC	38–42 HRC
Toughness	Excellent	Outstanding
Wear Resistance	Higher	Moderate
Thermal Fatigue	Excellent	Very good
Large Dies	Good	Excellent
Forging Applications	Very good	Excellent
Impact Resistance	Good	Superior
Aluminium Die Casting	Excellent	Good

H13/DB6 comparison table in die casting and extrusion; go with DB6 for large forging dies, hammer dies and heavy-impact work.

Advantages & Limitations

Advantages	Limitations
Excellent hot hardness	Higher material cost
High thermal fatigue resistance	Needs proper heat treatment
Excellent toughness	Harder to machine once hardened
Good wear resistance	Limited corrosion resistance
Good machinability when annealed	Large sections need controlled processing
Excellent dimensional stability
Long tool life

How to Choose the Right Grade

1. Match the grade to the application.

Application	Recommended Grade
Aluminium die casting	H13 (1.2344)
Brass die casting	H13
Hot forging dies	H11 (1.2343)
Hammer dies	DB6 (1.2714)
Extrusion dies	H13
Plastic mould inserts	ESR H13
Large forging blocks	DB6

Get the size right. Think about how long it’s how wide it is, how thick it is, Think about length, width, thickness, weight, machining allowance, and expected dimensional change during heat treatment.. Available forms include forged blocks, round bars, flat bars, ESR blocks and pieces that are already cut to size.

Settle on a delivery condition with your supplier — annealed, pre-hardened, hardened and tempered, soft annealed, or stress relieved. With your supplier.

Check the quality before you make a decision. Ask for testing results, spectrometer reports, material test certificates, heat-number traceability and confirmation of surface finish, straightness and mechanical properties.

Plan the amounts you need based on prototypes, regular production, yearly use, extra stock and any growth that is coming up.

Choose a supplier who can support you. One that has stock, imported materials, forged and ESR blocks, fast delivery, technical help, certificates and custom machining.

Certifications Worth Looking For

Certification	Purpose
ISO 9001	Quality management system
EN 10204 3.1	Material test certificate
Ultrasonic Testing (UT)	Detects internal defects
Spectrometer Analysis	Verifies chemical composition
Hardness Test Report	Confirms HRC/HB values
Heat Number Traceability	Tracks production batch

Why Manufacturing Quality Matters

How the steel is made has a direct line to how it performs on the shop floor. Controlled melting, refining, forging, annealing, hardening, tempering and inspection are what separate a die that lasts from one that fails early — particularly in die casting, hot forging, aluminium extrusion and heavy-duty tooling, where the cost of a bad batch shows up fast.

Key Takeaways

Controlled melting and refining keep the chemistry consistent.
Forging improves structural uniformity and toughness.
Annealing gets the material ready for machining.
Hardening builds the strength and hardness.
Tempering balances hardness against toughness.
UT, chemical analysis, hardness testing and dimensional inspection confirm quality before shipping.
MTCs and heat-number traceability give buyers the documentation they need.

Why Choose Virat Special Steels?

Virat Special Steels Pvt. Ltd. has been supplying manufacturers with quality imported tool steels for over 70 years.

Over 70 years of industry experience.
3,500+ tons of tool steel in stock, ready to use
Sourced from established international mills.
“Wide grade range: H13, H11, DB6, D2, D3, P20, M2, M35, and ESR grades“.
“Every order comes with an EN 10204 3.1 MTC”
“UT and spectrometer testing on all material”
“Cut-to-size and custom machining available”
“Fast delivery across India”
“Trusted by automotive, forging, aerospace, plastic moulding, railway, and heavy engineering customers”.

Our Supply Network Across India

We supply H13, DB6, H11, H12, H10 and H21 across major industrial hubs — Delhi, Gurugram, Faridabad, Noida, Ghaziabad, Jaipur, agra, Ahmedabad, Vadodara, Surat, Rajkot, Mumbai, Pune, Nashik, Indore, Bhopal, Rudrapur , Chennai, Coimbatore, Hyderabad, Kolkata, Jamshedpur, Secunderabad and Nellore — with standard and custom sizes, cut-to-size material, annealed or heat-treated condition, and material test certificates as required.

Conclusion

H13 and DB6 remain the two most dependable choices for high-temperature tooling, offering a solid mix of hardness, toughness, wear resistance, hot strength and thermal-fatigue resistance. Get the grade selection, heat treatment, machining and maintenance right, and both can deliver excellent tool life. We supply H13, DB6 and other tool steel grades across major industrial cities in India for a wide range of manufacturing needs.

Get a Quote

Looking for reliable H13, DB6 or other hot work tool steel? Virat Special Steels supplies round & flat bars, forged & rolled blocks, ESR/non-ESR blocks and cut-to-size material — complete with MTC, UT testing, spectro testing, custom machining, ready stock and PAN India delivery.

Call: +91-98140 21775 Email: info@viratsteels.com Locations: Gurgaon (Haryana) | Ludhiana (Punjab)

Frequently Asked Questions

1. What is Hot Work Tool Steel?

Alloy steel for tools and dies exposed to high temperatures, thermal cycling, wear and mechanical stress.

2. What are the primary types?

Typical grades are H13, H11, H12, H10 and H21 – H13 tool is the most common.

3. H13 tool steel – what is it?

A hot work Cr-Mo-V grade that is known for its excellent hot strength, toughness, wear resistance and thermal-fatigue resistance.

4. What is the HRC of H13?

44-54 HRC depending on the application and heat treatment condition.

5. What is the maximum service temperature of H13?

Typically up to around 550–600°C, depending on load, thermal cycling and cooling conditions. Confirm the exact limit with your supplier’s datasheet.

6. Is H13 material good for high temperature applications?

Yes, it is used heavily where there is high heat and heating and cooling over and over again.

7. Can H13 be machined?

Yes, if annealed. It is much more difficult to machine once hardened.

8. How to Improve H13 Machinability?

Use proper cutting tools. Use appropriate speeds and feeds. Use adequate cooling. Machine in the annealed state where possible.

9. What is H13 used for?

Die casting dies, extrusion dies, forging dies, hot punches, mandrels and other similar hot work tooling.

10. H13 wear resistant?

Yes, if they are heat treated properly and matched to the proper operating conditions.

11. Is H13 hard enough?

Yes, gives a good balance of hardness and toughness which is what you need in demanding die work.

12. What is resistance to thermal fatigue?

It’s the ability of the steel to be heat cycled over and over again without heat checking or cracking.

13. Is H13 heat treatable?

Yes. Usually it is hardened and tempered so that it can obtain the desired hardness, toughness and hot strength.

14. Is H13 air hardenable?

Yes, which means it can achieve high hardness by means of appropriate heat treatment without a drastic quench.

15. Can H13 be used for nitriding?

Yes, nitriding can improve surface hardness, wear resistance and die life in suitable applications.

16. What is the chemical composition of H13?

Carbon, silicon, manganese, chromium, molybdenum and vanadium. Chromium, molybdenum and vanadium do most of the work.

17. What is the difference between H11 and H13?

Both are hot working grades but H13 tool steels gives generally a better combination of hot hardness, wear resistance, toughness and thermal-fatigue resistance.

18. What’s the difference between H13 and D2?

D2 is a cold-work grade built primarily for high wear resistance. H13 tool steel is a hot-work grade.

19. Is H13 tool steels appropriate for die casting dies?

Yes, it is widely used for aluminum, zinc and magnesium die casting because of its resistance to thermal fatigue and its hot strength.

20. Can H13 tool steels be used for hot extrusion die?

Yes, commonly used for extrusion dies, mandrels and related tooling.